Typical general characteristics

Appearance

Transparent

Transparent

Transparent

Transparent

Transparent

Density @23℃

ISO 1183-1 A

1.08g/cm³

1.12g/cm³

1.15g/cm³

1.19g/cm³

1.26g/cm³

After addition of 1.2% DCBP (50%) and cured for 10min at 120℃ and post cure for 4h at 200℃

Hardness Shore A

DIN 53505

38

53

61

71

78

Tensile strength

DIN 53504 S 1

8.6Mpa

8.7Mpa

8.9Mpa

8.7Mpa

8.3.Mpa

Elongation at break

DIN 53504 S 1

539%

529%

421%

418%

170%

Tear Strength

ASTM D 624 B

18KN/m

24KN/m

22KN/m

19KN/m

15KN/m

Compression set

DIN ISO 815-B
  (22 h / 175 °C)

38%

36%

38%

40%

45%

Rebound elasticity

DIN 53512

58%

56%

54%

51%

47%

After addition of 0.6% DBPMH (95%) and cured for 10min at 170℃ and post cure for 4h at 200℃

Hardness Shore A

DIN 53505

42

50

62

70

81

Tensile strength

DIN 53504 S 1

9.5Mpa

9.6Mpa

9.2Mpa

9.2Mpa

9.2Mpa

Elongation at break

DIN 53504 S 1

770%

616%

518%

518%

210%

Tear Strength

ASTM D 624 B

21KN/m

26KN/m

26KN/m

22KN/m

18KN/m

Compression set

DIN ISO 815-B
  (22 h / 175 °C)

21%

19%

22%

25%

30%

Rebound elasticity

DIN 53512

56%

55%

56%

50%

45%

After addition of 0.3% PT2001A and 0.6% PT2001B cured for 10min at 130℃ and post cure   for 4h at 200℃

Hardness Shore A

DIN 53505

39

48

60

68

78

Tensile strength

DIN 53504 S 1

10.5Mpa

10.8

10.6Mpa

10.2Mpa

10.2Mpa

Elongation at break

DIN 53504 S 1

840%

678%

601%

589%

259%

Tear Strength

ASTM D 624 B

27KN/m

30KN/m

33KN/m

33KN/m

23KN/m

After addition of 1.2% DCBP (50%) and cured for 10min at 120℃ and post cure for 4h at 200℃ and after   aging 7days @200℃

Hardness Shore A

DIN 53505

47

55

66

76

86

Tensile strength

DIN 53504 S 1

8.2Mpa

7.8Mpa

7.5Mpa

7.4Mpa

6.5Mpa

Elongation at break

DIN 53504 S 1

367%

348%

325%

312%

110%